Different proportions of BF12 (aver

称重不同比例的BF12（平均晶粒度约为2毫米）和LMO（平均晶粒度约为10毫米），并使用变速球磨机混合24小时。将所得的粉末<br>过筛并再次用研钵和研钵与10e20wt％的水混合。将湿粉末置于30μl中。30 mm矩形或直径20 mm的圆柱形模具在120℃下施加55e70 MPa的压力10e40分钟以实现致密化。将粒料在120℃的干燥炉中放置24小时。表1列出了根据粒料的几何形状计算并与理论值比较的合成粒料的密度。

Different proportions of BF12 (average grain size of ~2 mm) and LMO (average grain size of ~10 mm) were weighed and mixed for 24 h using a variable speed ball mill. The resulting powders were<br>sieved and mixed again using a pestle and mortar with 10e20 wt% water. The wet powder was placed in either a 30  30 mm rectangular or 20 mm diameter cylindrical die applying 55e70 MPa pressure at 120℃ for 10e40 min to achieve densification. The pellets were left in a dry furnace at 120℃ for 24 h. The density of synthesised pellets calculated based on the geometry of the pellets and compared to theoretical values are listed in Table 1.

采用变速球磨机对不同比例的BF12（平均粒径为~2 mm）和LMO（平均粒径为~10 mm）进行称重和搅拌24 h。得到的粉末是<br>用杵和研钵与10e20 wt%的水筛分并再次混合。将湿粉末放入30  30 mm矩形或20 mm直径的圆柱形模具中，在120℃下施加55e70兆帕的压力10 e40分钟，以实现致密化。球团在120℃的干燥炉中放置24小时。根据球团的几何形状计算出的合成球团密度与理论值比较如表1所示。<br>